Magnesia cement

Magnesia cement

TU 5745-002-00241324-00

OKP code - 2692740

Magnesia cement (magnesia binder) - a kind of inorganic binder based on magnesium oxide, and shuts chloride and / or magnesium sulfate. The main advantages of magnesia cement - fast curing, high strength achieved, excellent adhesion to woodDue to the unique properties of magnesium cement is used for everything monolithic screed, for the production мagnesium oxide wallboard, abrasive wheels, making partitions, stair treads and drip plates, facing tiles, insulation products.

Advantages of magnesium cement:

  • high resistance to alkali and organic solvents, oils, salts;
  • increased fire resistance;
  • low thermal conductivity;
  • high wear resistance;
  • High flexural strength and compression;
  • Increased adhesion of the material with various kinds of inorganic and organic fillers.
Characteristics of the product
IndicatorValue
Compressive strength 200-250 kgf/cm2
Tensile strength in bending 30-50 kgf/cm2
Mark of water resistance W0-W2
Water resistance (softening coefficient) 0,5
Frost control composition 20-25 cycles without damage or destruction
Frost samples with additive 100-150 cycles without damage or destruction
The thermal conductivity in the dry state 0,77 W/m·°С (at a density 1700 kg/m3)
Abrasion 1,5 г/см2 (при плотности 1700 кг/м3)
Drying shrinkage 4-8 mm/m
Drying shrinkage additive composition with 1-2 mm/m

The test report

Reports, protocols, certificates